Copper Strip production process, method features and common problems to solve, including copper strip cold rolling, Copper Strip hot rolling, hot rolling defects and Copper Strip discoloration solution
Release time:2021-07-09Click:955
Guide reading: Copper tape is a very common metal components, often in electrical components, lamp, battery Cap, buttons, Seals, connectors and other places to see, the main role is conductive, thermal, corrosion-resistant equipment. There are six areas in copper strip production, they are furnace area, laboratory, cutting area, hot rolling area, water washing area and rolling plate area. The following small series and we talk about copper production process, production methods of cold rolling and hot rolling characteristics of some common problems, such as the problem of discoloration and shear indentation, we have a look at it!
1. Copper Strip production process flow
1. Making the embryo: According to the predetermined production goal, adding different amounts of zinc in the waste copper material in order to make different specifications of copper raw material. 2. Assay: In order to ensure the production of both qualified and economic benefits of the finished product, the accuracy of the assay results is particularly important. The duty of the laboratory is to inform the smelter of the test results quickly and accurately according to the copper block. 3. CUTTING: the complete copper strip is drawn by the hanging rope, placed on the special cutting table smoothly, cut by the cutting wheel saw, and then polished and smoothed by the copper strip washing machine, this is conducive to post-processing out of the copper strip surface smoothness and smoothness. 4. Hot Rolling: THE CUT Copper Strip is heated at 1000 °C, then over-hot rolled and pressed into 2.3 cm thick copper strip. 5, washing: each copper block after the first rolling step, because the surface impurities exist, in order to avoid affecting the quality of the finished product, must be again through the closed furnace again through the washing process. The washing area is divided into two pools according to their acidity. The high concentration was 6.8 °C, while the low concentration was 3.5 °C. The red spots on the surface of copper bar and copper strip can be washed away by the acid in the water washing tank, while the dark red spots are removed by the iron fine brush during the water washing, to give a distinct shine to the copper itself. The same rolling plate during the red spots and red spots still need to re-wash steps. Regularly check the acidity of the pool during washing, add acid in time to avoid too low acid content resulting in insufficient washing. 6. Rolling Plate: The Rolling Plate area is divided into 180 primary rolling and 110 intermediate rolling according to the roller area. According to the different sizes of the rollers, the hot rolled copper strip, which has been forged in a closed furnace, is processed from rough to fine by the above two steps.
Features of copper strip production method
1. Cold Rolling
(1) plastic deformation of copper strip.
(2) the pressure in the gap area is high, and there is pressure distribution, the maximum is 2700MPA.
(3) there is friction along the rolling direction and in the reverse rolling direction.
(4) the instantaneous temperature of roll gap is high, which can reach 200 ~ 300 °C.
(5) co-existence of rolling and sliding states.
2. ADVANTAGES OF HOT-ROLLED COPPER STRIP:
(1) hot-rolled Copper Strip can significantly reduce energy consumption and cost. The metal has high plasticity and low deformation resistance during hot rolling, so the energy consumption of hot rolling is greatly reduced.
(2) hot rolling can improve the processing properties of metals and alloys, that is, crushing the coarse grains in the casting state, significantly healing the cracks, reducing or eliminating the casting defects, transforming the as-cast structure into deformed structure, and improving the processing properties of the alloys.
(3) the hot rolling usually uses the big INGOT and the big reduction rolling, not only has improved the production efficiency, but also has created the condition for increasing the rolling speed and realizing the rolling process continuity and the automation.
3. Defects of Copper Strip hot rolling
(1) after hot rolling, non-metallic inclusions (mainly sulfides and oxides, as well as silicates) inside the metal are compressed into thin sheets and delaminated. Delamination deteriorates the tensile properties of the metal along the thickness direction and May Cause Interlaminar tearing when the weld contract. The local strain induced by weld shrinkage often reaches several times of the yield point strain, which is much larger than that induced by load.
(2) residual stress due to uneven cooling. The residual stress is a kind of self-balanced stress without external force, which is found in all kinds of hot-rolled steel sections. Although the residual stress is self-equilibrium, it still has some influence on the performance of metal under external force. Such as deformation, stability, anti-fatigue, and other aspects may have adverse effects.
(3) The mechanical properties of hot rolled products can not be precisely controlled, and the microstructure and properties of hot rolled products can not be uniform. The Strength Index is lower than that of the cold-cured products, but higher than that of the completely annealed products, and the plasticity index is higher than that of the cold-cured products.
(4) It is difficult to control the thickness and size of hot rolled products, and the Ra value of the surface of hot rolled products is generally 0.5 ~ 1.5 m. Therefore, hot-rolled products are generally used as cold-rolled blanks.
3.Solution to common problems of Copper Strip
1. Solution of discoloration of Copper Strip
(1) control the concentration of acid solution during pickling. When the oxide layer on the surface of annealed copper strip is washed off, the higher acid concentration does not make any sense. On the contrary, the high concentration of residual acid on the surface of the copper strip makes it difficult to wash off, and accelerates the pollution of the cleaning water, which results in the high concentration of residual acid in the cleaning water and the discoloration of the copper strip. Therefore, when determining the concentration of the pickling solution, the principle should be followed: on the premise that the oxide layer on the surface of the copper strip can be cleaned off, the concentration should be reduced as far as possible.
(2) control the electrical conductivity of pure water. Control the electrical conductivity of pure water, that is, control the content of chlorine ion and other harmful substances in pure water. It is safe to control the conductivity below 50 S/CM.
(3) control the electrical conductivity of hot cleaning water and passivator. The increase of conductivity of hot cleaning water and passivator mainly comes from the residual acid brought in by the running copper strip. Therefore, under the condition of ensuring the quality of pure water, the residual acid content can be controlled by controlling the electrical conductivity. According to many experiments, it is safe to control the conductivity of hot-cleaning water and passivator below 200 S/CM.
(4) ensure the copper strip is dry. Local sealing is carried out at the exit of the air cushion furnace coil, and a dehumidifier and an air conditioner are used in the local sealing device to control the humidity and temperature in the coil of the copper strip within a certain range
(5) passivating with passivating agent. Most copper processing plants now use Benzotriazole, or BTA (molecular formula: C6H5N3) , as a passivator. Practice has proved that it is a convenient, economical and practical passivator. When the copper strip passes through BTA solution, the oxide film on the surface reacts with BTA to form a compact complex, which protects the copper matrix.
2. The solution to the cutting indentation of copper strip is to prevent the cutting edge indentation, mainly according to the thickness of the Strip, soft and hard degree to choose a reasonable round knife and rubber peel ring outside diameter difference; When the width of the Strip is small, the thickness of the circular cutter should be selected reasonably to increase the width of the rubber stripping ring.
Source: The web
- Previous:The technological conditions of oxygen-free copper strip billet for horizontal continuous casting are studied in this paper from aspects of oxygen-free copper strip billet, horizontal continuous casting, optimization of technological parameters and so on
- Next:Deep good text, aluminum alloy material machining process analysis